This study was carried out to investigate the cause of pith-damaged wood formation, the state of growth, and difference of chemical composition of Japanese Larix(L. leptolepis Gorden). 1. Larix grew normaly to 10 years, and the volume increment was 32.4%. But it was gradually decreased to 19.4% from 11 to 13 years that the heartwood damage was occurred. Therefore, the volume increment was decreased 13%. The decayed wood was formed from fire wound portion of bark by forest fire. The volume loss from pith-dagmaged wood occurred by forest fire was more than 20%. 2, On the ash content, heartwood(0.05%) and pith-damaged wood(0.08%) was lower than sapwood(0.29%). The difference of extractive contents are considered the reason. It is considered that this ash content difference is depend upon the extractive contents among sap, heart and decayed wood parts. Holocellulose contents were from 54.3% to 59.3% and there were no difference among heartwood, pith-damaged wood, and sapwood, On the pentosan contents, heartwood(6.3%) and pith-damaged wood(6.6%) were higher than sapwood. Lignin contents of pith-damaged wood was tower than heartwood (34.4%). This seems to weaken all kinds of wood strength.