Cellulase 에 의한 목재당화에 (木材糖化) 관한 연구 - (Ⅰ) 기질 (基質) 처리의 효과 -
Studies on the Hydrolysis of Holocellulose with Trichoderma viride Cellulase - (1) Effect of the treated substrate -
정대성 , 민두식 ( Tae Seong Cheong , Du Sik Min )
UCI I410-ECN-0102-2008-520-002108191

In this study, enzymatic hydrolysis of the holocellulose from Alnus hirsuta (Spach) Rupr. (8-14 yr`s) was investigated using crude cellulase preparations of Trichoderma viride Pers. ex. Fr. SANK 16374. And conducted on the optimum condition of the treated substrate for saccharification. A strain of Trichoderma viride Pers. ex. Fr. SANK 16374 was found to be highly efficient for the cellulase productivity, especially in the submerged culture process. The culture medium used in this experiment was prepared from an extract of wheat bran consisting also of KH₂ PO₄ 10, (NH₄)₂ SO₄ 3, NaNO₃ 3, and MgSO₄7H₂O 0.5g/1. Cellulose powder (Toyo filter paper, 60 mesh) was found to be an importent factar for inducing the cellulase formation. And the cellulase produced in the culture fluid was salted out quantitatively by the use of ammonium sulfate (Fig. 1) Reducing sugar was determined by the Dinitrosalicylic acid (DNS) method, using reagents prepared according to the method of Sumner (1925). The results obtained were summerized as follows; 1. The method of delignification were treated by the Peracetic acid (PA) method, according to the method of Toyama (1970). The yield of holocellulose were decreased in accordance with increasing concentration of Peracetic acid solution; delignification of Alnus hirsuta Rupr. with 20% Peracetic acid was satisfied for 48 hours and 40%∼60% peracetic acid was satisfied for 24 hrs: 2. The substrate (holocellulose) was changed easely into fine powder with enzymatic hydrolysis and cellulase exhibits optimum activity on the reducing sugar formation from substrate at the range of 60-100 mesh. 3. The reducing sugar formation increased in accordance with increasing dry temperature on holocellulose substrate was found to be 190±5℃. 4. The optimal heat treated time of holocellulose substrate was found to be 45 min. for the reducing sugar formation showed the best products. The reducing sugar formation did not show statisticaly significent diflerences at 5% levels by heat treated time for 45 min. and 60 min.

[자료제공 : 네이버학술정보]
×