TMCP(Thermo Mechanical Control Process) steel was continuously cast (CC) by varying the argon gas flow rate and vacuum time in the Ruhrstahl Heraeus (RH) refining process. Using the CC specimens, the distribution of the inclusions and the mechanical properties were evaluated. A lot of oxides and Al-O type inclusions were observed. The average Vickers hardness did not show a constant, but showed dispersion in a certain range. The shape and scale parameters of the CC specimen with an argon gas flow rate of 160Nm³ and a vacuum time of 12 minutes was the best. Mechanical properties (tensile strength, yield strength and elongation) were consistent with the Weibull probability distribution analysis results. The impact resistance was the best for CC specimens with an argon flow rate of 140 Nm³ and a vacuum time of 12 minutes. Although the inclusions and mechanical properties of the CC specimens were evaluated according to the argon gas flow rate and vacuum time, these values were no significant difference.