In this paper, the performance evaluation of the vibration damping ratio according to the polymer mixing ratio of the polymer modified mortar used as the floor finishing material of the apartment building structure was evaluated. To compare the vibration damping rate, ordinary potland cement (OPC) mortar and polymer modified mortar (PMM) were prepared. In addition, the mixed polymer was mixed with Styrene Butadiene Rubber (SBR) liquid polymer with a solid content of about 49%. Accordingly, the W/C of the test specimen was adjusted and compounded, and the experiment was conducted by mixing 5 types of the test specimen: OPC-60, PMM-5%, PMM-10%, PMM-15%, and PMM-20%. . In addition, in order to adjust the W/C of the specimen, the fluidity of each specimen was set as 210 (±5) mm. The specimens measured density and flow in fresh mortar and after curing for 28 days, flexural strength, compressive strength and ultrasonic pulse were measured. The attenuation rate was shown. The experimental results showed that the density increased according to the mixing of the polymer, the flexural strength increased as the mixing rate of the polymer increased, and the compressive strength was decreased. In addition, it was shown that the vibration damping rate increases with the increase in the amount of polymer incorporated.