Pb(Sb_0.5Nb_0.5)x(Zr_0.51Ti_0.49)_1-xO₃ (abbreviation: PSN-PZT) ceramics were synthesized, using conventional bulk ceramic processing technology, with various PSN doping contents. The maximum density of PSN-PZT was 97% of the theoretical density in the samples sintered at 1,250℃. The maximum values of the piezoelectric properties achieved using the conventional processes were: k_p of 0.625, d₃₃ of 531 pC/N, and g₃₃ of 33 mV·m/N. Finally, we fabricated a piezo-speaker with the optimized PSN-PZT ceramics. The SPL of the speaker was measured at a distance of 1 m, with a driving voltage of 40 V_rms in the frequency range of ~300 Hz to 9 kHz. The measured SPL_max was at a very high level (95 dB), which was superior in quality in comparison with those of other commercial products.