In this study, a TiO₂ nanotube was grown on a titanium plate by using anodic oxidation method for the evaluation of TiO2 nanotube morphology. The TiO₂ nanotube was grown in an electrolyte containing ethylene glycol, 0.2 wt% of NH4F and 2 vol% of H₂O. Applied voltage varied from 30 to 70 V and the morphology of the TiO₂ nanotube was observed. After anodization, a TiO₂ nanotube plate was immersed in 35°C ethanol for 24 hours. Anatase and rutile crystal forms of TiO₂ nanoutbe were observed after annealing. 4-chrolobenzoic acid, a probe compound for OH radicals, was dissolved in H₂O in order to measure the OH radical. Liquid chromatography was used to check the concentration of the 4-chrolobenzoic acid. The OH radical generation by TiO₂ nanotube plate was proportionate to the length of the TiO₂ nanotube. Furthermore, when the number of TiO₂ nanotube plate increased, the OH radical generation increased as well.