Improvement of the mechanical properties of a commercial aluminium casting alloy, A356, was achieved through an optimised combination of alloying elements, modification, and heat treatment. 0.7 wt.% Cu and an additional 0.2 wt.% Mg were added to an Al-7Si-0.35Mg alloy for strengthening at both room and elevated temperatures, whilst a subsequent decrease in the ductility was compensated for by the modification of eutectic Si by Sr addition at a level of up to 110 ppm. It was found that the dissolution of Cu-rich or Mg-rich phases could be maximised by solid-solutionising an alloy with 40 ppm Sr at 530oC, increasing the tensile and yield strengths to 350 MPa and 297 MPa, respectively, with a reasonably high strain of 5% after peak-aging at 210oC. Further addition of Sr up to 110 ppm is, however, more likely to interfere with the dissolution of the Cu-rich or Mg-rich phases during solid solution treatment, resulting in a slight decrease in both tensile and yield strengths at room temperature. Besides the Cu addition, such undissolved phases, on the other hand, may contribute to elevated temperature strength at 200oC.