Using the spark plasma sintering process (SPS process), the WC-6wt.%Co hard materials were densified using an ultra fine WC-Co powder. The WC-Co was almost completely dense with a relative density of up to 100% after the simultaneous application of a pressure of 60 MPa and the DC pulse current for 3 min without any significant change in the grain size. The average grain size of WC that was produced through this experiment was about 0.2~0.8 μm. The hardness and fracture toughness were about 1816 kg/mm2 and 15.1 MPa·m1/2, respectively, for 60 MPa at 1200℃.