The recrystallization texture of axisymmetric ally deformed fcc metals having major <111> + minor <100> fibers and major <100> + minor <111> fibers is the <100> orientation. The evolution of the {100}<001> recrystallization texture from the {112}<111> deformation texture and near {031}<20 1 3> recrystallization texture from plane strain compressed bicrystal {123}<412> and the recrystallization texture of axisymmetrically deformed fcc metals have been discussed based on the energy release maximization theory in which the absolute maximum stress direction in deformed state becomes parallel to the minimum Young`s modulus direction after recrystallization.