Graft copolymerization of MMA/4-VP onto cotton fiber using Ce(IV) salt as an initiator and triton X-100 as an emulsifier was performed under various polymerization conditions. In cograft polymerization, the polymeization behavior according to variation of 4-VP feed composition and the characteristics of MMA/4VP graft polymer such as affinity for acid dye owing to cationization of cotton, antibacterial activity and thermal behavior were investigated. The results of this study were as follows; 1. While in copolymerization of MMA and 4-VP, 4-VP content in copolymer was more than that of monomer feed composition. 2. Increasing 4-VP content, graft yield was decreased, but graft efficiency was increased. In case of MMA/4VP graft polymerization, the highest graft yield was obtained at higher CAN concentration than in MMA graft polymerization, the reason is that the behavior of 4-VP was disturbed by Ce(IV) salt. 3. Elevation of temperature resulted in increase of graft yield and the apparent activation energy of MMA/4-VP graft polymerization was higher than that of MMA graft polymerization. 4. MMA/4-VP grafted cotton fiber showed affinity for acid dye, antibacterial activity and higher moisture regain than MMA grafted cotton fiber. MMA/4-VP grafted cotton fabric showed improvement of wrinkle recovery up to 40∼50% graft yield and decreased thereafter. MMA/4-VP and. MMA grafted cotton fabric did not showed significant difference in wrinkle recovery and stiffness.