Present work was carried out to investigate the influence of welded conditions, such as welding cur-rent, diameter of welding wire on the microstructural change and mechanical properties of TIG welded joint in AZ31B Mg alloy. It was found that good and sound welded joint was achieved in all welding conditions. The grain size decreased with increasing welding current and decreasing diameter of welding wire. Also, the second phases were homogeneously distributed in the grain and grain boundary as decreasing welding current and diameter of welding wire. The β discontinuos precipitates were observed in the welded joint, but this microstructure has not been reported by previous researchs in AZ31B Mg alloy. The hardness value is affected by the existence state of the second phase and the hardness of the welded joint region is lower than the other regions in welded AZ31B Mg alloy. The strength of the welded joint region was influenced by the grain size and has more than 90%, compared to that of ASTM standard specification.