Effects of sulfur and manganese on the hot workability of STS 316L and 309S steels have been investigated. From the results of hot workability test, the hot ductility was decreased with increasing sulfur content and reheating temperature. This is considered to be caused by sulfur segregations and sulfide precipitates at grain boundaries. Sulfur would be dissolved under the reheating conditions and reprecipitated with decreasing temperatures during hot rolling. The content of reprecipitated sulfur is decreased with increasing manganese content and decreasing reheating temperature. Therefore, the hot ductility is increased with increasing manganese content. It was also found that the hot ductility is increased with decreasing reheating temperature.