This study was performed to investigation the effect of austempering temperature on the mecanical properties and fracture Characteristic of the ductile cast iron with contains Cu and Mo. The obtained results of this study were as follows; Microstructure of austemped ductile cast iron obtained by sustempering were low bainite with some martensite at 250℃, mixture of low and upper bainite at 300℃ and upper bainite at 350℃. With increasing austempering temperature, yield strength, tensile strength and hardness decreased, while the elongation and impact absorption energy increased. With increasing austempering temperature, fracture toughness value increased and mainly controlled by bolume fraction of retained austenite. The volume fraction of retained austenite increased and the fracture surface obtained fibrous and dimple with increasing austempering temperature.