The adhesion strength of TiN films to substrate(STC 3) steel has been studied using the scratch adhesion test. Before deposition, the substrates were mechanically polished and TiN films were deposited at different substrate temperature (480℃-540℃). The chemical properties of TiN films were investigated by RBS, and EDS, and the physical properties were investigated by micro-hardness tester, SEM, and X-ray diffractometer. According to results of this study, the adhesion strength of TiN films increase with increasing the deposition temperature. The roughness of the polished substrates surface were measured with a profilometer. It was observed that, as a general rule, the adhesion strength of deposited TiN films increase with decreasing the substrates surface roughness.