폴리머 혼화제로서 styrene-butadiene rubber(SBR)라텍스, ethylene-vinyl acetate(EVA)에멀젼 및 polyacrylic ester(PAE)에멀젼을 사용하여 동일한 스럼프에서 폴리머-시멘트비를 변화시켜 공시체를 제조하여, 압축과 휨강도시험, 흡수시험, 세공분포측정 및 미세구조 관찰등을 실시하였다. 그 결과 폴리머-시멘트비의 증가와 더불어 압축과 휨강도 모두 향상되었고, 동해에 큰 영향을 주는 모세관 공극범위의 세공량은 감소되었으며, 폴리머 시멘트비 l5wt% 이상에서 연속적인 폴리머필름이 형성되었다.

Test specimens of polymer-cement concrete composites were prepared using styrene-butadiene rubber(SBR) latex, ethylenevinyl acetate(EVA) and polyacrylic ester(PAE) emulsions as polymer dispersions in cement modified system at constant slump(10±0.5cm), then compressive and flexural strengths water absorption, pore size distribution, and microstructures were investigated. Compressive and flexural strengths of these composites were remarkably improved with an increase of polymer-cement ratio. These composites had a desirable pore size distribution against frost damage due to a small capillary pore volume. Continuous polymer film was able to form in higher than 15% of polymer-cement ratio.