Evaluation of rolling contact fatigue damage as well as material development for roll of rolling mill is being studied until quite recently. In this paper, a focus has been imposed on evaluating the rolling contact fatigue damage. In order for this, the accumulating process of rolling contact damage using the ferritic, pearlitic and bainitic DCI has been analyzed by X-ray diffraction technique. The main finds are; 1) The graphite in DCI is considered to be a cause of interfering in the redistribution of stress. Eventually, it results in the branching of crack. 2) The evaluation of rolling contact fatigue damage can be estimated in terms of the change of residual stress and/or a half-value breadth on surface during rolling contact. (Received October 9, 1997)