Effects of high Si-P addition on microstructure and mechanical properties of thin ductile cast iron have been investigated. The amount of silicon addition have fixed on 4.0wt% and the amounts of phosphorus addition and thickness of specimen have been varied from 0.05 to 0.8wt% and ø13㎜, ø10㎜ and ø6㎜, respectively. As the casting thickness decreased, the average diameter of spheroidal graphite was decreased and the hardness of the cast iron increased. By adding P, the average diameter of spheroidal graphite was increased and the count of the spheroidal graphite was decreased continuously. And the tensile strength and the elongation was decreased, and the hardness was increased. With the P added more than 0.2wt%, the abraded amount was decreased significantly. The addition of P improved the wear resistance and the hardness of thin ductile cast iron.