Recently Al-Cu-P alloys are used to refine primary Si of hypereutectic Al-Si alloys. Because it has inside AlP compound that acts as nucleation site in the melt, Al-Cu-P alloy has good refinement effect in lower holding temperature and after shoter holding times. In this study Al-Cu-P refinement agent was made by mechanical alloying method. When Al-13.5wt%Cu-1.5wt%P was alloyed mechanically for 30hr in Ar atmosphere by high energy ball mill, it had the refinement effect that showed primary Si size of about 30㎛ in Al-20wt%Si at 760℃, treated for 15min.