Rapidly Solidified (RS) Al-Zr base splats with various alloy contents were prepared by atomization-splat quenching method to understand the continuous and discontinuous precipitation in the aged alloys. And the RS alloys were consolidated by hot extrusion and swaging to analyze the effect of plastic deformation on the precipitation behavior. Discontinuous precipitation dominated at relatively low temperature in the Al-Zr alloy, whereas both V additions to Al-Zr alloys and hot metal working appeared to suppress the discontinuous precipitation. As continuous precipitation is favored in the grain interiors, the driving force for discontinuous precipitation become to disappear with a further process.