The effects of weld repair on the durability in Al-10%Si-0.3%Mg castings were evaluated. The strength and fracture toughness in fusion zone were higher than those in the base metal by rapid cooling of fusion zone after welding. There were no significant differences between fatigue properties in castings and weld repaired specimen as the results of low cycle fatigue and rotating bending fatigue test. Therefore it was concluded that weld repairing did not have any significant effect on the mechanical properties of castings.