This study hay been carried out to investigate into the rolling wear characteristics of austempered ductile iron under unlubricated dry rolling condition by Amsler type test with 9.09% sliding ratio. Wear amount is increased with increasing of ferrite and retained austenite and it has been found that the amount of rolling wear is decreased when the hardness of matrix are higher. The rolling life up to generation of abnormal condition is conspicusly increased and amount of rolling wear is increased asrolling revolutionis increased and wear of austempered ductile ironunder dry rolling condition. Matrix has been obtained to upper bainite, low bainite at heat treatment, obtained to bull`s eye structure at as cast. It has been found that the amount of rolling wear is decreased when the tensile strength of the casting are increased and then the rolling life up to generation of abnormal wear in conspicuously increased and amount of wear was intend to graphite content.