The effects of pressure during solidification on macro-and micro-structures have been studied in pure aluminium and Al-Si alloys. The application of pressure during solidifcation accelerated both equiaxed and columnar dendritic-growth due to stimulating of equiaxed survival and faster preferential growth of primary dendrites against the parallel direction of heat flow. Burden-Hunt model was modified to express the significant changes of CET behaviours under pressure. A further point to be noted was that greatly fine eutectic silicon flakes (0.5×13㎛) with the decrease of halo layers (7㎛) of aluminium riched phases in the periphery of primary silicon particles were observed when pressure was applied during solidification.